We report a large third-order nonlinear optical response of palladium diselenide (PdSe2) films – a two-dimensional (2D) noble metal dichalcogenide material. Both open-aperture (OA) and closed-aperture (CA) Z-scan measurements are performed with a femtosecond pulsed laser at 800 nm to investigate the nonlinear absorption and nonlinear refraction, respectively. In the OA experiment, we observe optical limiting behaviour originating from large two photo absorption (TPA) in the PdSe2 film of β = 3.26 × 10-8 m/W. In the CA experiment, we measure a peak-valley response corresponding to a large and negative Kerr nonlinearity of n2 = -1.33×10-15 m2/W – two orders of magnitude larger than bulk silicon. We also characterize the variation of n2 as a function of laser intensity, observing that n2 decreases in magnitude with incident laser intensity, becoming saturated at n2 = -9.96×10-16 m2/W at high intensities. These results verify the large third-order nonlinear optical response of 2D PdSe2 as well as its strong potential for high performance nonlinear photonic devices.

Layered two-dimensional (2D) GO films are integrated with silicon-on-insulator (SOI) nanowire waveguides to experimentally demonstrate an enhanced Kerr nonlinearity, observed through self-phase modulation (SPM). The GO films are integrated with SOI nanowires using a large-area, transfer-free, layer-by-layer coating method that yields precise control of the film thickness. The film placement and coating length are controlled by opening windows in the silica cladding of the SOI nanowires. Owing to the strong mode overlap between the SOI nanowires and the highly nonlinear GO films, the Kerr nonlinearity of the hybrid waveguides is significantly enhanced. Detailed SPM measurements using picosecond optical pulses show significant spectral broadening enhancement for SOI nanowires coated with 2.2-mm-long films of 1−3 layers of GO, and 0.4-mm-long films with 5−20 layers of GO. By fitting the experimental results with theory, the dependence of GO’s n2 on layer number and pulse energy is obtained, showing interesting physical insights and trends of the layered GO films from 2D monolayers to quasi bulk-like behavior. Finally, we show that by coating SOI nanowires with GO films the effective nonlinear parameter of SOI nanowires is increased 16 fold, with the effective nonlinear figure of merit (FOM) increasing by about 20 times to FOM > 5. These results reveal the strong potential of using layered GO films to improve the Kerr nonlinear optical performance of silicon photonic devices.

Layered two-dimensional (2D) graphene oxide (GO) films are integrated with micro-ring resonators (MRRs) to experimentally demonstrate enhanced nonlinear optics in the form of four-wave mixing (FWM). Both uniformly coated and patterned GO films are integrated on CMOS-compatible doped silica MRRs using a large-area, transfer-free, layer-by-layer GO coating method together with photolithography and lift-off processes, yielding precise control of the film thickness, placement, and coating length. The high Kerr nonlinearity and low loss of the GO films combined with the strong light-matter interaction within the MRRs results in a significant improvement in the FWM efficiency in the hybrid MRRs. Detailed FWM measurements are performed at different pump powers and resonant wavelengths for the uniformly coated MRRs with 1−5 layers of GO as well as the patterned devices with 10−50 layers of GO. The experimental results show good agreement with theory, achieving up to ~7.6-dB enhancement in the FWM conversion efficiency (CE) for an MRR uniformly coated with 1 layer of GO and ~10.3-dB for a patterned device with 50 layers of GO. By fitting the measured CE as a function of pump power for devices with different numbers of GO layers, we also extract the dependence of GO’s third-order nonlinearity on layer number and pump power, revealing interesting physical insights about the evolution of the layered GO films from 2D monolayers to quasi bulk-like behavior. These results confirm the high nonlinear optical performance of integrated photonic resonators incorporated with 2D layered GO films.